Via structure having a metal hump for low interface resistance

ABSTRACT

A semiconductor device structure is provided. The semiconductor device structure includes a first insulating layer, a first metal via passing through the first insulating layer, and a second insulating layer formed over the first insulating layer. The semiconductor device structure also includes a first metal hump surrounded by the second insulating layer and connected to the top surface of the first metal via. The first metal hump covers the portion of the first insulating layer adjacent to the first metal via. In addition, the semiconductor device structure includes a metal line formed in the second insulating layer and electrically connected to the first metal via, and a conductive liner covering the first metal hump and separating the metal line from the second insulating layer and the first metal hump.

PRIORITY CLAIM AND CROSS-REFERENCE

This application claims the benefit of U.S. Provisional Application No. 62/906,909, filed on Sep. 27, 2019, and entitled “Interconnect structure with low resistance”, the entirety of which is incorporated by reference herein.

BACKGROUND

The semiconductor integrated circuit (IC) industry has experienced rapid growth. Technological advances in IC materials and design have produced generations of ICs where each generation has smaller and more complex circuits than the previous generation. As the semiconductor industry has progressed into nanometer technology process nodes in pursuit of higher device density, higher performance, and lower costs, challenges from both fabrication and design issues have resulted in the development of three-dimensional designs, such as the fin field effect transistor (FinFET). Advantages of the FinFET may include reducing the short channel effect and raising the current flow.

Although existing FinFET manufacturing processes have generally been adequate for their intended purposes, as device scaling-down continues, they have not been entirely satisfactory in all respects. For example, in the manufacturing of ICs, via structures are used for connecting to the source/drain contacts and gate contacts which are connected to source/drain regions and the gates of FinFETs. However, it is a challenge to form reliable via structures at smaller and smaller sizes.

BRIEF DESCRIPTION OF THE DRAWINGS

Aspects of the present disclosure are best understood from the following detailed description when read with the accompanying figures. It should be noted that, in accordance with standard practice in the industry, various features are not drawn to scale. In fact, the dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion.

FIGS. 1A to 1D illustrate perspective views of various stages of manufacturing a semiconductor device structure in accordance with some embodiments.

FIGS. 2A to 2I illustrate cross-sectional representations of various stages of manufacturing the semiconductor device structure in accordance with some embodiments. FIG. 2A is cross-sectional representation taken along 2-2′ line of FIG. 1D.

FIGS. 3A to 3I illustrate cross-sectional representations of various stages of manufacturing the semiconductor device structure in accordance with some embodiments. FIG. 3A is cross-sectional representation taken along 3-3′ line of FIG. 1D.

FIG. 4 illustrates a perspective view of a semiconductor device structure in accordance with some embodiments.

FIG. 5A illustrates a cross-sectional representation of a semiconductor device structure in accordance with some embodiments. FIG. 5A is cross-sectional representation taken along 5I-5I′ line of FIG. 4.

FIG. 5A-1 illustrates a cross-sectional representation of a semiconductor device structure in accordance with some embodiments.

FIG. 5A-2 illustrates a cross-sectional representation of a semiconductor device structure in accordance with some embodiments.

FIG. 5B illustrates a cross-sectional representation of a semiconductor device structure in accordance with some embodiments. FIG. 5B is cross-sectional representation taken along 5II-5II′ line of FIG. 4.

FIG. 6A illustrates a cross-sectional representation of a semiconductor device structure in accordance with some embodiments. FIG. 6A is cross-sectional representation taken along 6I-6I′ line of FIG. 4.

FIG. 6A-1 illustrates a cross-sectional representation of a semiconductor device structure in accordance with some embodiments.

FIG. 6A-2 illustrates a cross-sectional representation of a semiconductor device structure in accordance with some embodiments.

FIG. 6B illustrates a cross-sectional representation of a semiconductor device structure in accordance with some embodiments. FIG. 6B is cross-sectional representation taken along 6II-6II′ line of FIG. 4.

DETAILED DESCRIPTION

The following disclosure provides many different embodiments, or examples, for implementing different features of the subject matter provided. Specific examples of components and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. For example, the formation of a first feature over or on a second feature in the description that follows may include embodiments in which the first and second features are formed in direct contact, and may also include embodiments in which additional features may be formed between the first and second features, such that the first and second features may not be in direct contact. In addition, the present disclosure may repeat reference numerals and/or letters in the various examples. This repetition is for the purpose of simplicity and clarity and does not in itself dictate a relationship between the various embodiments and/or configurations discussed.

Furthermore, spatially relative terms, such as “beneath,” “below,” “lower,” “above,” “upper” and the like, may be used herein for ease of description to describe one element or feature's relationship to another element(s) or feature(s) as illustrated in the figures. The spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures. The apparatus may be otherwise oriented (rotated 90 degrees or at other orientations) and the spatially relative descriptors used herein may likewise be interpreted accordingly. It should be understood that additional operations can be provided before, during, and after the method, and some of the operations described can be replaced or eliminated for other embodiments of the method.

Embodiments for manufacturing semiconductor device structures are provided. The semiconductor device structures may include a metal via formed in a first insulating layer and connected to a gate electrode layer or a source/drain contact. A second insulating layer is formed over first insulating layer and has a trench opening exposing the top of the metal via. Afterwards, a metal hump is selectively formed over the exposed top of the metal via. Afterwards, a conductive liner is formed in the trench opening to cover the metal hump. A metal line is filled in the trench opening and over the conductive liner. Alternatively, the selectively formed metal hump fills the entire trench opening without the formation of the conductive liner and the metal line. In the case of the existence of the conductive liner, although the conductive liner has a higher resistance than that of the metal line and the metal via, the metal hump has a convex top surface and a plane bottom surface each of which has an area greater than the exposed top surface of the metal via. Therefore, the metal via with the metal hump thereon can provide a greater contact area for the metal line than the metal via without the metal hump formed thereon. As a result, the interface resistance between the conductive liner and the metal via can be reduced, thereby mitigating the electric current crowding. In the case of the entire trench opening is filled with the metal hump, such an interface resistance can be eliminated, thereby preventing the electric current crowding. Therefore, the device's performance can be improved.

FIGS. 1A to 1D illustrate perspective views of various stages of manufacturing a semiconductor device structure in accordance with some embodiments. Moreover, FIGS. 2A to 2I illustrate cross-sectional representations of various stages of manufacturing the semiconductor device structure in accordance with some embodiments. FIG. 2A is cross-sectional representation taken along 2-2′ line of FIG. 1D. In addition, FIGS. 3A to 3I illustrate cross-sectional representations of various stages of manufacturing the semiconductor device structure in accordance with some embodiments. FIG. 3A is cross-sectional representation taken along 3-3′ line of FIG. 1D. In some embodiments, the semiconductor device structure includes one or more transistors (e.g., fin field effect transistors (FinFETs)) and an interconnect structure electrically connected to the FinFETs. As shown in FIG. 1A, a substrate 100 is provided. In some embodiments, the substrate 100 is a semiconductor substrate, such as a bulk semiconductor, a semiconductor-on-insulator (SOI) substrate, or the like, which may be doped (e.g. with a P-type or an N-type dopant) or undoped. In some embodiments, the substrate 100 is a wafer, such as a silicon wafer. Generally, an SOI substrate includes a layer of a semiconductor material formed on an insulator layer. The insulator layer may be, for example, a buried oxide (BOX) layer, a silicon oxide layer, or the like. The insulator layer is provided on a substrate, typically a silicon or glass substrate.

Other substrates, such as a multi-layered or gradient substrate may also be used. In some embodiments, the semiconductor material of the substrate 100 includes silicon; germanium; a compound semiconductor including silicon carbide, gallium arsenic, gallium phosphide, indium phosphide, indium arsenide, and/or indium antimonide; an alloy semiconductor including SiGe, GaAsP, AlInAs, AlGaAs, GaInAs, GaInP, and/or GaInAsP; or a combination thereof. In some embodiments, the substrate 100 includes silicon. In some embodiments, the substrate 100 includes an epitaxial layer. For example, the substrate 100 has an epitaxial layer overlying a bulk semiconductor.

In some embodiments, the substrate 100 includes a PMOS region for P-type FinFETs formed thereon. The PMOS region of the substrate 100 may include Si, SiGe, SiGeB, or an III-V group semiconductor material (such as InSb, GaSb, or InGaSb). In some embodiments, the substrate 100 includes an NMOS region for N-type FinFETs formed thereon. The NMOS region of the substrate 100 may include Si, SiP, SiC, SiPC, or an III-V group semiconductor material (such as InP, GaAs, AlAs, InAs, InAlAs, or InGaAs). In some other embodiments, the substrate 100 includes the PMOS region and the NMOS region.

Afterwards, a fin structure 101 and an isolation feature 103 are successively formed over the substrate 100, as shown in FIG. 1A in accordance with some embodiments. In some embodiments, the substrate 100 is patterned to form the fin structure 101. The isolation feature 103 is a shallow trench isolation (STI) structure, and the fin structure 101 is surrounded by the isolation feature 103. The isolation feature 103 may be formed by depositing an insulating layer (not shown) over the substrate 100 and recessing the insulating layer. The insulating layer for the formation of the isolation feature 103 may be made of silicon oxide, silicon nitride, silicon oxynitride, fluorosilicate glass (FSG), low-K dielectric materials, and/or another suitable dielectric material and may be deposited by a flowable CVD (FCVD) process, a chemical vapor deposition (CVD) process, an atomic layer deposition (ALD) process, or another applicable process.

Afterwards, dummy gate structures 111 a, 111 b, 111 c, and 111 d are formed across the fin structure 101 over the substrate 100 to cover the isolation feature 103, as shown in FIG. 1A in accordance with some embodiments. Each of the dummy gate structures 111 a, 111 b, 111 c, and 111 d includes a dummy gate dielectric layer 104 and a dummy gate electrode layer 106 formed over the dummy gate dielectric layer 104. As an example, the dummy gate dielectric layer 104 may be made of silicon oxide, and the dummy gate electrode layer 106 may be made of polysilicon.

Afterwards, insulating spacers (e.g., gate spacers 108) are formed on the opposite sidewalls of each of the dummy gate structures 111 a, 111 b, 111 c, and 111 d, in accordance with some embodiments. Each gate spacer 108 may include a single layer or a multiple structure. In some embodiments, the gate spacer 108 includes a single layer, as shown in FIG. 1A. In some embodiments, the gate spacer 108 is made of is made of SiO, HfSi, SiOC, AlO, ZrSi, AlON, ZrO, HfO, TiO, ZrAlO, ZnO, TaO, LaO, YO, TaCN, SiN, SiOCN, ZrN, or SiCN. The gate spacer 108 may have a thickness that is in a range from about 5 nm to about 30 nm. The insulating layer may be formed by performing a chemical vapor deposition (CVD) process, a plasma enhanced CVD (PECVD) process, low-pressure CVD (LPCVD) process, an atomic layer deposition (ALD) process, or another applicable process.

After formation of the gate spacers 108, source/drain regions 110 (which are also referred to as source/drain features) are formed in the fin structure 101 laterally adjacent to and exposed from the dummy gate structures 111 a, 111 b, 111 c, and 111 d, as shown in FIG. 1A in accordance with some embodiments. In some embodiments, the source/drain regions 110 is formed by recessing the portions of the fin structure 101 laterally adjacent to the dummy gate structures 111 a, 111 b, 111 c, and 111 d and growing semiconductor materials in the formed recesses in the fin structure 101 by performing epitaxial (epi) growth processes. For example, the semiconductor device structure may be an NMOS device, and the source/drain regions 110 may include Si, SiP, SiC, SiPC, or an III-V group semiconductor material (such as InP, GaAs, AlAs, InAs, InAlAs, or InGaAs), or the like. Alternatively, the semiconductor device structure may be a PMOS device, and the source/drain regions 110 may include Si, SiGe, SiGeB, or an III-V group semiconductor material (such as InSb, GaSb, or InGaSb), or the like. The source/drain regions 110 protrude above the isolation feature 103, as shown in FIG. 1A.

After the source/drain regions 110 are formed, an insulating layer 112 is formed over the fin structure 101 of the substrate 100 and covers the isolation feature 103 and the source/drain regions 110, as shown in FIG. 1B in accordance with some embodiments. The insulating layer 112 may serve as an interlayer dielectric (ILD) layer) and may be a single layer or include multiple dielectric layers with the same or different dielectric materials. For example, the insulating layer 112 may be a single layer made of silicon oxide, tetraethyl orthosilicate (TEOS), phosphosilicate glass (PSG), borosilicate glass (BSG), boron-doped phosphosilicate Glass (BPSG), fluorosilicate glass (FSG), undoped silicate glass (USG), or the like. The insulating layer 112 may be deposited using any suitable method, such as a chemical vapor deposition (CVD) process, a plasma enhanced CVD (PECVD) process, flowable CVD (FCVD) process, the like, or a combination thereof.

Afterwards, the dummy gate structures 111 a, 111 b, 111 c, and 111 d are removed and replaced by gate structures 118 a, 118 b, 118 c, and 118 d, as shown in FIG. 1B in accordance with some embodiments. In some embodiments, each of the adjacent gate structures 118 a, 118 b, 118 c, and 118 d includes a gate dielectric layer 114, a gate electrode layer 116, and the gate spacers 108. The gate dielectric layer 114 may be made of metal oxides, metal nitrides, metal silicates, transition metal-oxides, transition metal-nitrides, transition metal-silicates, oxynitrides of metals, or other applicable dielectric materials.

In some embodiments, the gate electrode layer 116 is made of a conductive material, such as aluminum, copper, tungsten, titanium, tantalum, or another applicable material. Each of the gate structures 118 a, 118 b, 118 c, and 118 d may further include a work functional metal layer (not shown) between the gate dielectric layer 114 and the gate electrode layer 116, so that the gate structures 118 a, 118 b, 118 c, and 118 d have the proper work function values. The work function metal layer may be made of TiN, TaN, Ru, Mo, Al, WN, ZrSi₂, MoSi₂, TaSi₂, NiSi₂, WN, or a combination thereof. Alternatively, the work function metal layer may be made of Ti, Ag, TaAl, TaAlC, TiAlN, TaC, TaCN, TaSiN, Mn, Zr, or a combination thereof.

The gate structures 118 a, 118 b, 118 c, and 118 d are etched to form recesses 119, as shown in FIG. 1C in accordance with some embodiments. During the etching, top portions of the gate dielectric layers 130 and the gate spacers 108 are also etched, so that upper sidewalls of the insulating layer 112 are exposed by the recesses 119. In some embodiments, each of the gate electrode layers 116 is further etched after the upper sidewalls of the insulating layer 112 are exposed. As a result, the top surface of each gate spacer 108 and the top surface of each gate dielectric layer 114 are higher than the top surface of the corresponding gate electrode layer 116, as shown in FIG. 1C.

Afterwards, a conductive capping feature (not shown) is optionally formed to cover each of the recessed gate electrode layers 116, in accordance with some embodiments. The conductive capping features and the underlying gate electrode layer 116 form gate stacks of the gate structures 118 a, 118 b, 118 c, and 118 d. In some embodiments, the top surface of each gate spacer 108 is higher than the top surface of each gate stack. The conductive capping features protect the gate electrode layers 116 from damage or loss during subsequent processing. In some embodiments, the conductive capping features are made of a metal material, such as tungsten or fluorine-free tungsten.

Afterwards, insulating capping layers 120 a, 120 b, 120 c, and 120 d are formed in the recesses 119 (not shown and as indicated in FIG. 1C) to respectively cover the top surfaces of the gate structures 118 a, 118 b, 118 c, and 118 d, as shown in FIG. 1D in accordance with some embodiments. In some embodiments, an insulating layer (not shown) used for formation of the insulating capping layers 120 a, 120 b, 120 c, and 120 d is formed over the structure shown in FIG. 1C and fills the recesses 119. For example, the insulating layer is made of a material that is different from the material of the insulating layer 112. For example, insulating layer is made of SiO, HfSi, SiOC, AlO, ZrSi, AlON, ZrO, HfO, TiO, ZrAlO, ZnO, TaO, LaO, YO, TaCN, SiN, SiOCN, Si, ZrN, or SiCN. The insulating layer may have a thickness that is less than or substantially equal to about 50 nm. The insulating layer may be formed by performing a chemical vapor deposition (CVD) process, a plasma enhanced CVD (PECVD) process, low-pressure CVD (LPCVD) process, an atomic layer deposition (ALD) process, or another applicable process. In some embodiments, a polishing process, such as a chemical mechanical polishing (CMP) process, is performed to remove the excess insulating layer above the insulating layer 112. The polishing process is performed on the insulating layer until the insulating layer 112 is exposed and planarized. As a result, the remaining insulating layers in the recesses 119 form insulating capping layers 120 a, 120 b, 120 c, and 120 d. The top surfaces of the insulating capping layers 120 a, 120 b, 120 c, and 120 d are substantially level with the top surface of the insulating layer 112, as shown in FIGS. 1D, 2A and 3A. The insulating capping layers 120 a, 120 b, 120 c, and 120 d serve as etch stop layers and protect the gate structures 118 a, 118 b, 118 c, and 118 d in the subsequent manufacturing processes (e.g., etching processes).

After the formation of the insulating capping layers 120 a, 120 b, 120 c, and 120 d, a masking layer (not shown) is formed over the insulating layer 112 and covers the insulating capping layers 120 a, 120 b, 120 c, and 120 d, in accordance with some embodiments. In some embodiments, the masking layer includes a tri-layer resist structure including a bottom layer, a middle layer, and a top layer. More specifically, the bottom layer may contain a material that is patternable and/or have anti-reflection properties, such as a bottom anti-reflective coating (BARC) layer. The middle layer (which is also referred to as a hard mask layer) provides hard mask properties for the photolithography process. The middle layer may be made of silicon nitride, silicon oxynitride or silicon oxide. The top layer may be a positive photoresist or negative photoresist. In some other embodiments, the tri-layer resist structure includes oxide-nitride-oxide (ONO) layers.

Afterwards, self-aligned openings are formed through the masking layer and the insulating layer 112 to expose the top surfaces of some source/drain regions 110 between the gate structures 118 a and 118 b, between the gate structures 118 b and 118 c, and between the gate structures 118 c and 118 d, in accordance with some embodiments. In some embodiments, the self-aligned openings are formed by patterning the masking layer and the insulating layer 112. During the patterning of the insulating layer 112, the insulating capping layers 120 a, 120 b, 120 c, and 120 d are used as etch masks, so as to define source/drain contact regions 110 between the gate structures 120 a, 120 b, 120 c, and 120 d.

Afterward, a conductive material (not shown) is formed over the patterned masking layer and fills the self-aligned openings, in accordance with some embodiments. In some embodiments, the conductive material is made of Co, W, Ru, Ni, Rh, Al, Mo, Cu, or a metal compound, or the like. The conductive material may be formed by a chemical vapor deposition (CVD) process, a physical vapor deposition, (PVD) process, an atomic layer deposition (ALD) process, an electroless deposition (ELD) process, an electrochemical plating (ECP) process, or another applicable process.

A polishing process, such as chemical mechanical polishing (CMP) process, is performed on the conductive material 155 until the insulating capping layers 120 a, 120 b, 120 c, and 120 d are exposed and planarized, in accordance with some embodiments. As a result, the remaining conductive material forms a source/drain contact 124 a between and laterally adjacent to the gate structures 118 a and 118 b, a source/drain contact 124 b between and laterally adjacent to the gate structures 118 b and 118 c, and a source/drain contact 124 c between and laterally adjacent to the gate structures 118 c and 118 d, as shown in FIGS. 2B and 3B. Those source/drain contacts 124 a, 124 b, and 124 c are electrically connected to the corresponding source/drain regions 110 and therefore they are also referred to as self-aligned source/drain contacts or self-aligned source/drain electrodes. Afterwards, the masking layer is removed.

Afterwards, the source/drain contacts 124 a, 124 b, and 124 c are etched to form recesses (not shown), in accordance with some embodiments. As a result, the top surfaces of the source/drain contacts 124 a, 124 b, and 124 c are lower than the top surfaces of the insulating capping layers 120 a, 120 b, 120 c, and 120 d and the top surfaces of the insulating spacers (i.e., gate spacers 108).

After the source/drain contacts 124 a, 124 b, and 124 c are recessed, insulating capping layers 126 a, 126 b, 126 c, and 126 d are formed in the recesses to cover the source/drain contacts 124 a, 124 b, and 124 c, respectively, as shown in FIGS. 2B and 3B in accordance with some embodiments. In some embodiments, each of the insulating capping layers 126 a, 126 b, 126 c, and 126 d has a top surface that is substantially level to the top surfaces of the insulating capping layers 120 a, 120 b, 120 c, and 120 d. In some embodiments, each of the insulating capping layers 126 a, 126 b, 126 c, and 126 d has a thickness that is less than or substantially equal to 50 nm. Moreover, the insulating capping layers 126 a, 126 b, 126 c, and 126 d are made of a material that is different from the material of the insulating capping layers 120 a, 120 b, 120 c, and 120 d and the material of the gate spacers 108. For example, the insulating capping layers 126 a, 126 b, 126 c, and 126 d are made of SiO, HfSi, SiOC, AlO, ZrSi, AlON, ZrO, HfO, TiO, ZrAlO, ZnO, TaO, LaO, YO, TaCN, SiN, SiOCN, Si, ZrN, or SiCN. The insulating capping layers 126 a, 126 b, 126 c, and 126 d may be formed by performing a deposition process (e.g., chemical vapor deposition (CVD) process, a plasma enhanced CVD (PECVD) process, low-pressure CVD (LPCVD) process, an atomic layer deposition (ALD) process, or another applicable process) followed by a polishing process (e.g., a chemical mechanical polishing (CMP) process).

After the formation of the insulating capping layers 126 a, 126 b, 126 c, and 126 d, insulating layers 130 and 132 are successively formed over the insulating layer 112 and cover the insulating capping layers 126 a, 126 b, 126 c, and 126 d, as shown in FIGS. 2C and 3C in accordance with some embodiments. In some embodiments, the insulating layer 130 serves as an etch stop layer and is made of SiN, SiCN, SiOC, SiON, SiCN, or SiOCN. The insulating layer 130 may be formed by performing a chemical vapor deposition (CVD) process, a plasma enhanced CVD (PECVD) process, low pressure CVD (LPCVD) process, an atomic layer deposition (ALD) process, or another applicable processes.

In some embodiments, the insulating layer 132 includes a single layer or multilayers and is made of SiO₂, SiOC, ZrO₂, HfO₂, or another applicable dielectric material, or a combination thereof. The insulating layer 132 serves as an interlayer dielectric (ILD) layer and is made of silicon oxide, tetraethyl orthosilicate (TEOS), phosphosilicate glass (PSG), borosilicate glass (BSG), boron-doped phosphosilicate Glass (BPSG), fluorosilicate glass (FSG), undoped silicate glass (USG), or the like. The insulating layer 132 may be formed by performing by any suitable deposition method, such as a chemical vapor deposition (CVD) process, a plasma enhanced CVD (PECVD) process, flowable CVD (FCVD) process, physical vapor deposition, (PVD), atomic layer deposition (ALD), spin-on coating, the like, or a combination thereof.

After the insulating layer 132 is formed, one or more via openings are formed and pass through the insulating layer 132, the insulating layer 130, the insulating capping layers 120 a and 120 b, and the insulating capping layers 126 a and 126 b. In some embodiments, via openings 136 a and 136 b that pass through and are surrounded by the insulating layer 132, the insulating layer 130, the insulating capping layers 120 a and 120 b, and the insulating capping layers 126 a and 126 b are formed, so as to expose the top surfaces of the source/drain contacts 124 a and 124 b, as shown in FIG. 2D. Similarly, via openings 138 a and 138 b that pass through and are surrounded by the insulating layer 132, the insulating layer 130, the insulating capping layers 120 a and 120 b, and the insulating capping layers 126 a and 126 b are formed, so as to expose the top surfaces of the gate electrode layers 116 of the gate structures 118 b and 118 c, as shown in FIG. 3D in accordance with some embodiments.

In some embodiments, those via openings 136 a, 136 b, 138 a, and 138 b are formed by performing photolithography and etching processes. For example, an etching process (such as a dry etching process) may be performed using the insulating layer 130 as an etch stop layer after the photolithography process, so that openings through the insulating layer 132 are formed and the insulating layer 130 is exposed. Afterwards, one or more etching processes (such as dry etching processes) may be performed to etch the insulating layer 130 and the insulating capping layers 120 a, 120 b, 126 a, and 126 b. In some other embodiments, the via openings 136 a and 136 b and the via openings 138 a, and 138 b are formed by respective photolithography processes and etching processes. In other words, the via openings 136 a and 136 b may be formed before or after the formation of the via openings 138 a, and 138 b.

After the formation of the via openings 136 a, 136 b, 138 a, and 138 b, metal vias 140 a and 140 b are formed in the via openings 136 a and 136 b (not shown and as indicated in FIG. 2D), and metal vias 142 a and 142 b are formed in the via openings 138 a and 138 b (not shown and as indicated in FIG. 3D), as respectively shown in FIGS. 2E and 3E in accordance with some embodiments. More specifically, a conductive material (not shown) is formed over the insulating layer 132 and fills the via openings 136 a, 136 b, 138 a, and 138 b, in accordance with some embodiments. The conductive material may be made of metal, such as W, Ru, Co, Cu, or another suitable metal material and formed by a chemical vapor deposition (CVD) process, a physical vapor deposition, (PVD) process, an atomic layer deposition (ALD) process, an electroless deposition (ELD) process, an electrochemical plating (ECP) process, or another applicable process.

Afterwards, a polishing process is performed to remove the excess conductive material, so that the insulating layer 132 are exposed and planarized. In some embodiments, the polishing process includes a chemical mechanical polishing (CMP) process. The insulating layer 132 has a top surface that is substantially level with the top surface of the remaining conductive material. After the polishing process, the remaining conductive material forms metal vias 140 a, 140 b, 142 a, and 142 b, as shown in FIGS. 2E and 3E in accordance with some embodiments. In some embodiments, the metal vias 140 a, 140 b, 142 a, and 142 b has a height that is in a range from about 1 nm to 50 nm, and has a width that is in a range from about 5 nm to 25 nm.

As shown in FIG. 2E, the metal vias 140 a and 140 b are in direct contact with the source/drain contacts 124 a and 124 b, respectively, to electrically connect the corresponding source/drain regions 110. Therefore, each of the metal vias 140 a and 140 b may be referred to as a source/drain via structure. As shown in FIG. 3E, the metal vias 142 a and 142 b are in direct contact with and electrically connected to the gate electrode layers 116 of the gate structures 118 b and 118 c. Therefore, each of the metal vias 142 a and 142 b may be referred to as a gate via structure.

After the formation of metal vias 140 a, 140 b, 142 a, and 142 b, an insulating layer 150 is formed over the insulating layer 132 and covers the metal vias 140 a, 140 b, 142 a, and 142 b, as shown in FIGS. 2F and 3F in accordance with some embodiments. In some embodiments, the insulating layer 150 serves as an inter-metal dielectric (IMD) layer and is made of SiN, SiCN, SiOC, SiON, SiCN, or SiOCN. The insulating layer 150 may be formed by performing a chemical vapor deposition (CVD) process, a plasma enhanced CVD (PECVD) process, low pressure CVD (LPCVD) process, an atomic layer deposition (ALD) process, or another applicable processes.

Afterwards, one or more trench openings are formed and pass through the insulating layer 150. In some embodiments, a trench opening 152 that passes through the insulating layer 150 is formed, so as to expose the top surfaces of the metal vias 140 a and 140 b (i.e., the source/drain via structures), as shown in FIG. 2G. Similarly, a trench opening 154 that passes through the insulating layer 150 is also formed, so as to expose the top surfaces of the metal vias 142 a and 142 b (i.e., the gate via structures), as shown in FIG. 3G in accordance with some embodiments.

In some embodiments, those trench openings 152 and 154 are formed by performing photolithography and etching processes. For example, an etching process (such as a dry etching process) may be performed using the insulating layer 132 as an etch stop layer after the photolithography process, so that trench openings 152 and 154 through the insulating layer 150 are formed and the insulating layer 132 is exposed.

After the trench openings 152 and 154 are formed, selectively growing metal humps from top surfaces of the corresponding metal vias, as shown in FIGS. 2H and 3H in accordance with some embodiments. In some embodiments, metal humps 160 a and 160 b are formed in the trench opening 152 and surrounded by the insulating layer 150, as shown in FIG. 2H. The formed metal humps 160 a and 160 b are connected to top surfaces of the metal vias 140 a and 140 b, respectively. Moreover, the metal humps 160 a and 160 b cover a portion of the insulating layer 132 adjacent to the corresponding metal vias 140 a and 140 b. In some embodiments, each of the metal humps 160 a and 160 b has a convex top surface and a plane bottom surface. The convex top surfaces and the plane bottom surfaces of the metal humps 160 a and 160 b have an area greater than each of the exposed top surface of the metal vias 140 a and 140 b. The metal humps 160 a and 160 b may be made of a material that is the same as or different than the material of the metal vias 140 a and 140 b. For example, the metal humps 160 a and 160 b may be made of W, Ru, Co, Cu, or another suitable metal material. The metal humps 160 a and 160 b may be formed by a selective deposition technology. For example, a metal inhibition layer (not shown), such as an organic film including amphiphilic-like molecules, conformally covers the top surface of the insulating layer 150 and the inner surface of the trench opening 152 and exposes the top surface of the metal vias 140 a and 140 b. Afterwards, a deposition process (such as a chemical vapor deposition (CVD) process, an atomic layer deposition (ALD) process, an electroless deposition (ELD) process, an electrochemical plating (ECP) process, or another applicable process) may be performed, so that the metal humps 160 a and 160 b are selectively and directly deposited on and connected to the metal vias 140 a and 140 b, respectively, due to the formation of the metal inhibition layer. During the formation of the metal humps 160 a and 160 b, the metal inhibition layer may be consumed. The remaining metal inhibition layer (if presented) may be entirely removed by, for example, plasma dry etching, chemical etching removal, ashing, etching and ashing, or wet etching using high-temperature sulfuric peroxide mixture (SPM) after the formation of the metal humps 160 a and 160 b. In some embodiments, the metal humps 160 a and 160 b each is grown to the desired thickness. For example, each of the metal humps 160 a and 160 b has a height that is less than or substantially equal to 50 nm. In some embodiments, the metal humps 160 a and 160 b are spaced apart from each other.

Similarly, metal humps 162 a and 162 b are formed in the trench opening 154 and surrounded by the insulating layer 150, as shown in FIG. 3H. The formed metal humps 162 a and 162 b are connected to top surfaces of the metal vias 142 a and 142 b, respectively. Moreover, the metal humps 162 a and 162 b cover a portion of the insulating layer 132 adjacent to the corresponding metal vias 142 a and 142 b. In some embodiments, the metal humps 1602 a and 162 b each also has a convex top surface and a plane bottom surface that have an area greater than each of the exposed top surface of the metal vias 142 a and 142 b. The material and the method used for the formation of the metal humps 162 a and 162 b are the same as those used for the formation of the metal humps 160 a and 160 b. In some embodiments, the metal humps 162 a and 162 b are formed during the formation of the metal humps 160 a and 160 b. In some embodiments, the metal humps 162 a and 162 b each is grown to the desired thickness. For example, each of the metal humps 162 a and 162 b has a height that is less than or substantially equal to 50 nm. In some embodiments, the metal humps 162 a and 162 b are also spaced apart from each other.

After the formation of the metal humps 160 a, 160 b, 162 a, and 162 b, a conformal conductive layer 166 and a fill metal material 168 are successively formed over the insulating layer 150 and fills the trench opening 152 (not shown and as indicated in FIG. 2H) and the trench opening 154 (not shown and as indicated in FIG. 3H), as shown in FIGS. 2I and 3I in accordance with some embodiments. In some embodiments, the conformal conductive layer 166 covers the metal humps 160 a, 160 b, 162 a, and 162 b and separates the fill metal material 168 from the insulating layer 150 and the metal humps 160 a, 160 b, 162 a, and 162 b.

In some embodiments, the conformal conductive layer 166 is made of or includes TaN, TiN, TiO, TaO, TiSiN, or a combination thereof. In some embodiments, the conformal conductive layer 166 is formed using a chemical vapor deposition (CVD) process, an atomic layer deposition (ALD) process, a physical vapor deposition (PVD) process, one or more other applicable processes, or a combination thereof.

In some embodiments, the fill metal material 168 and the conformal conductive layer 166 are made of different materials. In some embodiments, the fill metal material 168 is made of or includes Cu, Co, Ru, W, one or more other suitable materials, or a combination thereof. In some embodiments, the fill metal material 168 is formed using an electroplating process, a physical vapor deposition (PVD) process, a chemical vapor deposition (CVD) process, an electroless plating process, one or more other applicable processes, or a combination thereof.

The conformal conductive layer 166 with a sufficient thickness (for example, in a range from about 3 nm to 20 nm) can protect the insulating layer 150 from diffusion of metal atoms from the fill metal material 168 during subsequent thermal processes or cycles. Moreover, the conformal conductive layer 166 may serve as a glue layer to enhance the adhesion between the insulating layer 150 and the fill metal material 168, thereby preventing the fill metal material 168 from peeling during the subsequent planarization process.

Although the conformal conductive layer 166 can improve the reliability of the fill metal material 168, the interface resistance between the metal vias 140 a, 140 b, 142 a, and 142 b and the subsequently formed conductive feature (which includes the conformal conductive layer 166 and the fill metal material 168) is increased due to high resistance of the conformal conductive layer 166 and small size of the metal vias 140 a, 140 b, 142 a, and 142 b. However, as mentioned, each of the metal humps 160 a, 160 b, 162 a, and 162 b having a convex top surface and a plane bottom surface helps to increase the contact area between the metal vias 140 a, 140 b, 142 a, and 142 b and the subsequently formed conductive feature, so as to reduce the contact resistance between the metal vias 140 a, 140 b, 142 a, and 142 b and the subsequently formed conductive feature. Therefore, the reliability of the subsequently formed conductive feature can be improved while reducing the interface resistance between the metal vias 140 a, 140 b, 142 a, and 142 b and the subsequently formed conductive feature.

After the conformal conductive layer 166 and the fill metal material 168 shown in FIGS. 2I and 3I are formed, a planarization process is performed, as shown in FIGS. 4, 5A, 5B, 6A, and 6B in accordance with some embodiments. FIG. 4 illustrates a perspective view of a semiconductor device structure in accordance with some embodiments. FIG. 5A is cross-sectional representation taken along 5I-5I′ line of FIG. 4. FIG. 5B is cross-sectional representation taken along 5II-5II′ line of FIG. 4. FIG. 6A is cross-sectional representation taken along 6I-6I′ line of FIG. 4. FIG. 6B is cross-sectional representation taken along 6II-6II′ line of FIG. 4.

In some embodiments, the planarization process removes the conformal conductive layer 166 and the fill metal material 168 above the insulating layer 150. The remaining portions of the conformal conductive layer 166 and the fill metal material 168 in the trench openings of the insulating layer 150 to form a metal line 180 with a conductive liner 170, a metal line 182 with a conductive liner 172, a metal line 184 with a conductive liner 174, and a metal line 186 with a conductive liner 176, as shown in FIGS. 4, 5B, and 6B. In some embodiments, the planarization process includes a chemical mechanical polishing (CMP) process. The formed metal lines 180, 182, 184, and 186 may have a height that is in a range from about 1 nm to 50 nm.

In some embodiments, the metal line 180 is electrically connected to the metal vias 140 a and 140 b, and the conductive liner 170 is formed between metal hump 160 a from the metal hump 160 b to separate the metal hump 160 a from the metal hump 160 b, as shown in FIG. 5A. Moreover, the conductive liner 170 covers the metal humps 160 a and 160 b and separates the metal line 180 from the insulating layer 150 and the metal humps 160 a and 160 b, as shown in FIG. 5B.

FIG. 5A-1 illustrates a cross-sectional representation of a semiconductor device structure in accordance with some embodiments. The semiconductor device structure shown in FIG. 5A-1 is similar to the semiconductor device structure shown in FIG. 5A. In some embodiments, the materials, formation methods, and/or benefits of the semiconductor device structure shown in FIG. 5A may also be applied in the embodiments illustrated in FIG. 5A-1, and are therefore not repeated. Unlike the metal humps 160 a and 160 b in the semiconductor device structure shown in FIG. 5A, the metal humps 160 a′ and 160 b′ in the semiconductor device structure shown in FIG. 5A-1 are laterally merged with each other, in accordance with some embodiments.

FIG. 5A-2 illustrates a cross-sectional representation of a semiconductor device structure in accordance with some embodiments. The semiconductor device structure shown in FIG. 5A-2 is similar to the semiconductor device structure shown in FIG. 5A. In some embodiments, the materials, formation methods, and/or benefits of the semiconductor device structure shown in FIG. 5A may also be applied in the embodiments illustrated in FIG. 5A-2, and are therefore not repeated. Unlike the metal humps 160 a and 160 b in the semiconductor device structure shown in FIG. 5A, the metal humps (nor shown) in the semiconductor device structure shown in FIG. 5A-2 are laterally merged with each other and completely fill the trench opening (not shown) that is formed in the insulating layer 150, in accordance with some embodiments. In those cases, the merged metal hump 160 serves as a metal line connected to the metal vias 140 a and 140 b, and therefore the steps for the formation of the conformal conductive layer and the fill metal material can be skipped. That is, the interface resistance between the metal line (that is formed of the merged metal hump 160) and the metal vias 140 a and 140 b can be greatly reduced.

In some embodiments, the metal line 182 is electrically connected to the metal vias 142 a and 142 b, and the conductive liner 172 is formed between metal hump 162 a from the metal hump 162 b to separate the metal hump 162 a from the metal hump 162 b, as shown in FIG. 6A. Moreover, the conductive liner 172 covers the metal humps 162 a and 162 b and separates the metal line 182 from the insulating layer 150 and the metal humps 162 a and 162 b, as shown in FIG. 6B.

FIG. 6A-1 illustrates a cross-sectional representation of a semiconductor device structure in accordance with some embodiments. The semiconductor device structure shown in FIG. 6A-1 is similar to the semiconductor device structure shown in FIG. 6A. In some embodiments, the materials, formation methods, and/or benefits of the semiconductor device structure shown in FIG. 6A may also be applied in the embodiments illustrated in FIG. 6A-1, and are therefore not repeated. Unlike the metal humps 162 a and 162 b in the semiconductor device structure shown in FIG. 6A, the metal humps 162 a′ and 162 b′ in the semiconductor device structure shown in FIG. 6A-1 are laterally merged with each other, in accordance with some embodiments.

FIG. 6A-2 illustrates a cross-sectional representation of a semiconductor device structure in accordance with some embodiments. The semiconductor device structure shown in FIG. 6A-2 is similar to the semiconductor device structure shown in FIG. 6A. In some embodiments, the materials, formation methods, and/or benefits of the semiconductor device structure shown in FIG. 6A may also be applied in the embodiments illustrated in FIG. 6A-2, and are therefore not repeated. Unlike the metal humps 162 a and 162 b in the semiconductor device structure shown in FIG. 6A, the metal humps (nor shown) in the semiconductor device structure shown in FIG. 6A-2 are laterally merged with each other and completely fill the trench opening (not shown) that is formed in the insulating layer 150, in accordance with some embodiments. In those cases, the merged metal hump 162 serves as a metal line connected to the metal vias 142 a and 142 b, and therefore the steps for the formation of the conformal conductive layer and the fill metal material can be skipped. That is, the interface resistance between the metal line (that is formed of the merged metal hump 162) and the metal vias 142 a and 142 b can be greatly reduced.

Embodiments of semiconductor device structures and methods for forming the same are provided. The formation of the semiconductor device structure includes forming a metal via in a first insulating layer. Afterwards, a metal hump is selectively formed over the top surface of the metal via and surrounded by the second insulating layer. Afterwards, a conductive liner is formed in the second insulting layer to cover the metal hump, and a metal line is formed over the conductive liner in the second insulting layer. The metal hump has a convex top surface and a plane bottom surface each of which has an area greater than the exposed top surface of the metal via. Therefore, the metal via with the metal hump thereon can provide a greater contact area for the metal line than the metal via without the metal hump formed thereon. As a result, the interface resistance between the conductive liner and the metal via can be reduced, thereby mitigating the electric current crowding. Accordingly, the device's performance can be improved.

In some embodiments, a semiconductor device structure is provided. The semiconductor device structure includes a first insulating layer, a first metal via passing through the first insulating layer, and a second insulating layer formed over the first insulating layer. The semiconductor device structure also includes a first metal hump surrounded by the second insulating layer and connected to the top surface of the first metal via. The first metal hump covers the portion of the first insulating layer adjacent to the first metal via. In addition, the semiconductor device structure includes a metal line formed in the second insulating layer and electrically connected to the first metal via, and a conductive liner covering the first metal hump and separating the metal line from the second insulating layer and the first metal hump.

In some embodiments, a semiconductor device structure is provided. The semiconductor device structure includes a fin structure over a substrate. The semiconductor device structure also includes a first insulating layer over the substrate and covering the fin structure, a first gate electrode layer in the first insulating layer and across the fin structure, and a first source/drain contact electrically connected to the first source/drain region in the fin structure. The semiconductor device structure further includes a second insulating layer over the first insulating layer, a first metal via and a second metal via passing through the second insulating layer and respectively connected to the first gate electrode layer and the first source/drain contact. In addition, the semiconductor device structure includes a first metal hump and a second metal hump respectively connected to the top surface of the first metal via and the top surface of the second metal via, a first metal line and a second metal line respectively electrically connected to the first metal via and the second metal via. The semiconductor device structure also includes a first conductive liner and a second conductive liner. The first conductive liner separates the first metal line from the first metal hump. The second conductive liner separates the second metal line from the second metal hump.

In some embodiments, a method for forming a semiconductor device structure is provided. The method includes forming a first insulating layer over a substrate having a fin structure, forming a first gate electrode layer in the first insulating layer and across the fin structure, and forming a first source/drain contact electrically connected to the first source/drain region in the fin structure. The method also includes forming a second insulating layer over the first insulating layer and etching the second insulating layer to form a first via opening exposing the first gate electrode layer and a second via opening exposing the first source/drain contact. The method further includes forming a first metal via in the first via opening to connect the first gate electrode layer, and a second metal via in the second via opening to connect the first source/drain contact. In addition, the method includes forming a third insulating layer over the second insulating layer and etching the third insulating layer to form a first trench opening exposing the first metal via, and a second trench opening exposing the second metal via. The method also includes selectively growing a first metal hump from the top surface of the first metal via and a second metal hump from the top surface of the second metal via.

The fins described above may be patterned by any suitable method. For example, the fins may be patterned using one or more photolithography processes, including double-patterning or multi-patterning processes. Generally, double-patterning or multi-patterning processes combine photolithography and self-aligned processes, allowing patterns to be created that have, for example, pitches smaller than what is otherwise obtainable using a single, direct photolithography process. For example, in one embodiment, a sacrificial layer is formed over a substrate and patterned using a photolithography process. Spacers are formed alongside the patterned sacrificial layer using a self-aligned process. The sacrificial layer is then removed, and the remaining spacers may then be used to pattern the fins.

The foregoing outlines features of several embodiments so that those skilled in the art may better understand the aspects of the present disclosure. Those skilled in the art should appreciate that they may readily use the present disclosure as a basis for designing or modifying other processes and structures for carrying out the same purposes and/or achieving the same advantages of the embodiments introduced herein. Those skilled in the art should also realize that such equivalent constructions do not depart from the spirit and scope of the present disclosure, and that they may make various changes, substitutions, and alterations herein without departing from the spirit and scope of the present disclosure. 

What is claimed is:
 1. A semiconductor device structure, comprising: a first insulating layer; a first metal via passing through the first insulating layer; a second insulating layer formed over the first insulating layer; a first metal hump surrounded by the second insulating layer and connected to a top surface of the first metal via, wherein the first metal hump covers a portion of the first insulating layer adjacent to the first metal via; a metal line formed in the second insulating layer and electrically connected to the first metal via; and a conductive liner covering the first metal hump and separating the metal line from the second insulating layer and the first metal hump.
 2. The semiconductor device structure as claimed in claim 1, further comprising: a second metal via passing through the first insulating layer; and a second metal hump surrounded by the second insulating layer and connected to a top surface of the second metal via, wherein the second metal hump covers a portion of the first insulating layer adjacent to the second metal via.
 3. The semiconductor device structure as claimed in claim 2, wherein the first metal hump has a convex top surface and a plane bottom surface each of which has an area greater than the top surface area of the first metal via, and the second metal hump has a convex top surface and a plane bottom surface each of which has an area greater than a top surface area of the second metal via.
 4. The semiconductor device structure as claimed in claim 2, wherein the metal line is electrically connected to the second metal via, and wherein the conductive liner covers the second metal hump and separates the second metal hump from the metal line and the first metal hump.
 5. The semiconductor device structure as claimed in claim 2, wherein the second metal hump is laterally merged with the first metal hump, wherein the metal line is electrically connected to the second metal via, and wherein the conductive liner covers the second metal hump and separates the metal line from the second metal hump.
 6. The semiconductor device structure as claimed in claim 2, further comprising: a first transistor and a second transistor formed below the first insulating layer; a first source/drain contact connected between the first metal via and a first source/drain region of the first transistor; and a second source/drain contact connected between the second metal via and a second source/drain region of the second transistor.
 7. The semiconductor device structure as claimed in claim 6 further comprising: insulating spacers on opposite sides of the first source/drain contact and opposite sides of the second source/drain contact, wherein the insulating spacers protrude from a top surface of the first source/drain contact and a top surface of the second source/drain contact; a first insulating capping layer formed between first insulating layer and the first source/drain contact and surrounding the first metal via; and a second insulating capping layer formed between the first insulating layer and the second source/drain contact and surrounding the second metal via.
 8. The semiconductor device structure as claimed in claim 2, further comprising a first gate electrode layer and a second gate electrode layer formed below the first insulating layer and connected to the first metal via and the second metal via, respectively.
 9. The semiconductor device structure as claimed in claim 8, further comprising: insulating spacers on opposite sides of the first gate electrode layer and opposite sides of the second gate electrode layer, wherein the insulating spacers protrude from a top surface of the first gate electrode layer and a top surface of the second gate electrode layer; a first insulating capping layer formed between the first insulating layer and the first gate electrode layer and surrounding the first metal via; and a second insulating capping layer formed between first insulating layer and the second gate electrode layer and surrounding the second metal via.
 10. The semiconductor device structure as claimed in claim 1, wherein the first metal hump has a convex top surface and a plane bottom surface each of which has an area greater than a top surface area of the first metal via.
 11. A semiconductor device structure, comprising: a fin structure over a substrate; a first insulating layer over the substrate and covering the fin structure; a first gate electrode layer in the first insulating layer and across the fin structure; a first source/drain contact electrically connected to a first source/drain region in the fin structure; a second insulating layer over the first insulating layer; a first metal via and a second metal via passing through the second insulating layer and respectively connected to the first gate electrode layer and the first source/drain contact; a first metal hump and a second metal hump respectively connected to a top surface of the first metal via and a top surface of the second metal via; a first metal line and a second metal line respectively electrically connected to the first metal via and the second metal via; a first conductive liner separating the first metal line from the first metal hump; and a second conductive liner separating the second metal line from the second metal hump.
 12. The semiconductor device structure as claimed in claim 11, further comprising: a second gate electrode layer in the first insulating layer and across the fin structure; a second source/drain contact electrically connected to a second source/drain region in the fin structure; a third metal via and a fourth metal via passing through the second insulating layer and respectively connected to the second gate electrode layer and the second source/drain contact; and a third metal hump and a fourth metal hump respectively connected to a top surface of the third metal via and a top surface of the fourth metal via, wherein the first metal line and the second metal line are respectively electrically connected to the third metal via and the fourth metal via; and wherein the first conductive liner separates the first metal line from the third metal hump, and the second conductive liner separates the second metal line from the fourth metal hump.
 13. The semiconductor device structure as claimed in claim 12, wherein the first metal hump and the third metal hump each of which has a convex top surface and are separated from each other by the first conductive liner, and wherein the second metal hump and the fourth metal hump each of which has a convex top surface and are separated from each other by the second conductive liner.
 14. The semiconductor device structure as claimed in claim 12, wherein the first metal hump and the third metal hump are laterally merged with each other, and the second metal hump and the fourth metal hump are laterally merged with each other.
 15. A semiconductor device structure, comprising: a first conductive feature and a second conductive feature formed on a first insulating layer and adjacent to each other; a second insulating layer over the first insulating layer; a first metal via and a second metal via passing through the second insulating layer and respectively connected to the first conductive feature and the second conductive feature; a first metal hump and a second metal hump respectively capping a top surface of the first metal via and a top surface of the second metal via; and a metal line covering the first metal hump and the second metal hump.
 16. The semiconductor device structure as claimed in claim 15, further comprising: a conductive liner separating the metal line from the first metal hump and the second metal hump.
 17. The semiconductor device structure as claimed in claim 16, wherein the conductive liner separates the first metal hump from the second metal hump.
 18. The semiconductor device structure as claimed in claim 16, further comprising: a third insulating layer formed over the second insulating layer, wherein the conductive liner, the metal line, the first metal hump, and the second hump are formed in the third insulating layer, and wherein the conductive liner separates the metal line from the second insulating layer and the third insulating layer.
 19. The semiconductor device structure as claimed in claim 15, each of the first metal hump and the second metal hump has a convex top surface and a plane bottom surface each of which has an area greater than the top surface area of the first metal via and the second metal via.
 20. The semiconductor device structure as claimed in claim 15, wherein both of the first conductive feature and the second conductive feature comprises a gate electrode layer or a source/drain contact. 